Maxtech SI8760 Two Component Waterproof Liquid Silicone Gel Cable Junction Box Potting
∎Product Description
SI8760 is two-component transparent self-healing silicone gel, when cured it will become an elastomer with buffer and self-recovery property. Used to isolate moisture and another noxious pollutant from contacting the circuit board, also used as a dielectric of high voltage. The other usage is a stress relief for protecting the circuit and interconnect devices from high temperature and mechanical stress.
∎Key Features
-
1:1 addition type, good adhesive strength and self-healing
-
High elongation, excellent flexibility for mechanical stress relieving
-
Low oil penetration after cured, good anti-poisoning property
-
Good dielectric in high temperature for high voltage protection
-
Excellent aging resistance and weatherability
-
Excellent waterproof, corrosion prevention, moisture-proof and chemical media resistance
Cable Junction Box Silicone Gel Splice Kit Connector Silicone Electrical Potting and Encapsulation Sealants
Two-component silicone gel
Encapsulating Potting Gel Seal Compound
Cable Junction Box Silicone Gel Splice Kit Connector Silicone Electrical Potting and Encapsulation Sealants
∎Typical Applications
●Used for encapsulation of various modules, semi-conductor, IGBT, automotive ECU module, IC chip, weighing sensor, waterproof connector.
 |
|---|
 |
 |
 |
 |
 |
 |
 |
 |
∎Technical Data Table
PROPERTY STANDARD/UNITS VALUE of SI8760
---- ---- PART A PART B
Material ---- Polysiloxane Hydrogen polysiloxane
Color Visual inspection Light Blue.Colorless Liquid Colorless Liquid
Viscosity 25°C, cps 800 700
Density 25°C, g/cm3 0.99 0.99
Mixture/mass ratio ---- A:B=100:100
Viscosity of mixture 25°C, cps 750
Operation time 25°C, min 60
Cure condition ---- 25℃,24hours or 80℃, 30min
Cured appearance ---- Transparent gel
Penetration 1/mm 100
Dielectric strength KV/mm 25
Volume resistance DC500V, ohm-cm 1.0×1015
Loss factor 1 MHz ＜0.001
Dielectric constant 1 MHz 2.8
Application temperature °C -60~260
Note：All above data were tested under standardized conditions or tested by further experiments.
How to use ?
-
Mix Part A and Part B by 1:1 mass ratio, after evenly mixed, pouring directly into the components or modules as per requirements.
-
Still the potted component to let out the bubbles. It can be cured by heat, about 30mins in 80°C. The fixture time is about 4-5 hours when curing under room temperature. Require 24 hours to achieve surface without obvious oil layer.
-
Vacuum defoaming can improve the performance of cured product.
-
Seal the remaining products tightly after use.
-
Low temperature will slow the curing speed; heat curing is recommended.
-
It's hard for SI8760 to cure if contact with sulfur, amine or Sn
∎Packing Specification
-
●Part A—10 KG/Bucket
-
●Part B—10 KG/ Bucket.
∎Transport &Storage
● When stored at or below 25°C in the original unopened containers, this product has a usable life of 12 months from the date of production. A sampling test is necessary for products that exceed shelf life before taking use.
It’s non-dangerous goods, can be transported as normal chemicals, CAUTION leakage during transport.